Molecular design, fabrication, and properties of the new quinary ZGBCP electrolyteAs illustrated in Fig. 1a, water molecules show a strong solvation effect on the Zn2+, which has been demonstrated to be the main cause of hydrogen evolution reaction (HER) and dendrite formation in traditional ZnSO4 aqueous electrolyte13. Same phenomenon is observed in the Zn(BF4)2-based aqueous electrolyte (AE)14. In particular, except for the solvation effect of Zn2+ cations, the water molecules can attack BF4− anions and lead to hydrolysis of the anions based on the reaction (1), thus exacerbating corrosion and HER side reactions at the Zn anode/electrolyte interface15.$${{{{{\rm{BF}}}}}}_{4}^{-}+{{{{{\rm{H}}}}}}_{2}{{{{\rm{O}}}}}\leftrightarrow {{{{{\rm{BF}}}}}}_{3}{\left({{{{\rm{OH}}}}}\right)}^{-}+{{{{{\rm{F}}}}}}^{-}+{{{{{\rm{H}}}}}}^{+}$$
(1)
Fig. 1: Challenges of traditional aqueous electrolytes and unique characteristics of the ZGBCP electrolyte.a The interfacial issues of the aqueous electrolyte and traditional modification strategies. b Molecular design, fabrication, and unique properties of the ZGBCP electrolyte.Even though the solvation effect from water can be alleviated based on the organic solvent replacement according to the previously reported strategies, new issues of sluggish kinetics for Zn2+ at low temperatures and corrosion/decomposition for the BF4− anions at high temperatures have arisen16. To address the challenges as shown in Fig. 1a, a new quinary electrolyte system, ZGBCP hydrogel, was developed to realize the regulation of both Zn2+ cations and BF4− anions. First, glycerol, chitosan (CS), and polyacrylamide (PAM) with rich O and N atoms can form multiple strong hydrogen bonding with water molecules and influence the solvation structure of Zn2+ cations. Second, boric acid is capable of capturing HF and F−, thus suppressing the corrosion induced by BF4− anions based on the reaction such as (2)17,18,19:$${{{{\rm{BF}}}}}{{\left({{{{\rm{OH}}}}}\right)}_{3}}^{-}\leftrightarrow {{{{\rm{B}}}}}{\left({{{{\rm{OH}}}}}\right)}_{3}+{{{{{\rm{F}}}}}}^{-}$$
(2)
Moreover, three types of reactions: reversible esterification reaction between glycerol and boric acid (Supplementary Fig. 1)20, 21, protonation of chitosan and polymerization of acrylamide are involved in the synthetic process of the ZGBCP electrolyte. The delicate molecular design renders the electrolyte multiple unique properties: ‘liquid-like’ high conductivity, ‘gel-like’ robust interfacial adhesion, ‘solid-like’ high Zn2+ transfer number and robust mechanical strength (Fig. 1b).First, as seen in Fig. 2a, the ZGBCP electrolyte exhibits a conductivity of 28.7 mS cm−1 at room temperature, which is comparable to the AE (34.11 mS cm−1), and it maintains high conductivity over a wide temperature range from −50 to +80 °C. The unique hydrogen bonding network also endows the electrolyte superior water retention of 97.5% after exposing to the ambient air for nearly 50 days (Fig. 2b) as well as exceptional thermal stability towards extreme temperature and flaming conditions (Supplementary Fig. 3). Additionally, the designed dual cross-linking network with multiple hydrogen bonding network exhibit significant energy dissipation behavior through deformation flow, since the boric acid-glycerol reaction can facilitate the polymer mobility effectively as illustrated in Fig. 2c22, 23. This feature is advantageous for facilitating rapid ion transport and mitigating the volumetric expansion of the Zn anodes during the high-rate charge and discharge process24, 25.Fig. 2: The characterization of ion-conductive, mechanical, and thermal properties of different electrolytes.a Ionic conductivities of four electrolytes at different temperatures from −50 to +80 °C. The difference between ZGBCP, ZCP, or ZGP electrolytes is that the ZCP or ZGP does not contain glycerol and boric acid or boric acid and chitosan. b, Water-retention capability of the ZGBCP and AE electrolyte. c The variation of storage modulus G’ and loss modulus G” with strain oscillation of PAM/CS cross-linking network with/without the boric acid and glycerol. d Demonstration of ZGBCP electrolyte adhering to 5 × 5 cm2 Zn anodes and PANI cathodes at different temperatures. e The optical images of the interface between the PANI cathode and ZGBCP or ZCP electrolyte. f Adhesion work tests of the ZGBCP, ZGP, and ZCP electrolytes (inset: schematic diagram of AFM tapping mode). g Schematic illustration of the adhesive mechanism of ZGBCP electrolyte.Moreover, the ZGBCP electrolyte achieves robust interfacial adhesion effortlessly to many common materials such as zinc, stainless steel, carbon cloth, carbon paper, and polyaniline (PANI) with a large area of 5 × 5 cm² but a tiny contact area of 0.5 cm² (Fig. 2d and Supplementary Fig. 4). Remarkably, even at −40 and 80 °C, the adhesion shows no change (Fig. 2d). The adhesion force of the ZGBCP to the Zn electrode reaches as high as 8.9 kPa, which is higher than other two electrolytes (Supplementary Fig. 5). Moreover, the optical microscope images reveal that ZGBCP electrolyte shows much better adhesion interface than the ZGP and ZCP electrolytes (Fig. 2e and Supplementary Fig. 6), which is consistent with the highest adhesion work (778 mN m−1) characterized by the atomic force microscopy testing (Fig. 2f). Fundamentally, this can be attributed to the multiple electrostatic and weak intermolecular interactions induced by the esterification and protonation process in the ZGBCP electrolyte (Fig. 2g)26,27,28,29. Besides, the faster motion of the chain segment tuned by the esterification also helps the adhesive groups (–OH, –NH2, and –CONH2) diffuse dynamically to form a consistently robust adhesion. In addition, the polymerization of AM can enhance the crosslinking density, ensuring the reinforced stability between the electrolyte and the electrode. In summary, all three reactions are essential for the robust interface of the ZGBCP electrolyte with electrodes.Theoretical calculation and characterizations of the ZGBCP electrolyte and understanding of CRACSS strategy in solvation regulationTo gain insights into the CRACSS strategy and correlate the structure with the property of the ZGBCP electrolyte, theoretical calculation and experimental characterizations of the molecular and solvation structure of the cations and anions were performed. Firstly, detailed density functional theory (DFT), together with molecular dynamics (MD) simulations were conducted to investigate the impact of the CRACSS strategy on the solvation structure. For the cationic solvation structure, the PAM (−1.24 eV) and glycerol (−1.09 eV) show higher affinity to Zn2+ than H2O (−0.64 eV) and even near to the binding energy of 2H2O–Zn2+, which enables the reconstruction of the cationic solvation structure through replacing H2O to suppress the HER side reactions (Fig. 3a and Supplementary Fig. 7b). According to MD simulations, compared to the solvation structure Zn(BF4−)0.8(H2O)5.2 found in the AE, a new cationic coordination configuration (Zn2+(BF4−)1.4(H2O)3.6(C3H8O3)0.6PAM0.4, simplified as [Zn2+(BF4−)(H2O)4(C3H8O3)]+-PAM is formed in the ZGBCP electrolyte (Fig. 3b and Supplementary Fig. 8). Besides, the reductive tendency of H2O can be effectively suppressed, due to the much more balanced electrostatic potential (ESP) distribution of the distal coordinated H2O in the new configuration (Fig. 3c). Furthermore, the DFT calculations indicate that the electrostatic interaction energies (denoted as the H+ dissociation energy barrier) for H in the H2O of the solvation structure have been increased by approximately 2 eV compared to the [Zn2+(BF4−)(H2O)5]+ referring to Supplementary Fig. 8c, which also proves the suppressed HER tendency tuned by the reconstruction of the cationic solvation structure. In addition, the Supplementary Fig. 10 reveals the lowest solvation energy of [Zn2+(BF4−)(H2O)4(C3H8O3)]+-PAM (−9.11 eV) compared to other potential solvation structures, confirming the validity of MD results. Another two potential solvation structures without the polymer involved: [Zn2+(H2O)5(C3H8O3)]2+ (solvent-separated ion pairs, SSIP) and [Zn2+(BF4−)(H2O)4(C3H8O3)]+ (CIP) also show lower HER tendency in comparison with [Zn2+(BF4−)(H2O)5]+ and [Zn2+(H2O)6]2+ in the AE as illustrated in Supplementary Figs. 11 and 12. Although it is a small amount for CS, a new AGG solvation structure [Zn2+(BF4−)2(H2O)2(C3H8O3)]-CS was found near the CS chain segment due to its stronger affinity to both cations and anions, which is conducive to the desolvation process with highest H+ dissociation energy barrier (Supplementary Fig. 13). What’s more, as illustrated in Supplementary Fig. 14, the results of MD simulations based on the PAM and CS pentamer models are consistent with those results based on the trimer models, further verifying the validity of MD simulations.Fig. 3: Theoretical analysis and experimental characterization of the solvation structures and electrochemical stability of different electrolytes.a Binding energy of Zn2+ and BF4− with species including H2O, glycerol, boric acid, and PAM based on the B3LYP/6-311 + +g(d,p) level DFT calculations. b Cationic radial distribution function g(r) and coordination number n(r) different ligands. c The ESP distribution of cationic solvation structures based on the B97-3c level DFT calculations. d The n(r) of F of BF4− to the H of the H2O in the ZGBCP and AE electrolytes. e distribution of anions with different solvation configurations. f Activation energy Ea based on the fitting of ln Rct−1 versus 1000/T Arrhenius curves. g Transfer number test of the Zn2+ (tZn2+). h LSV curves of different electrolytes.The solvation environment of anions also has a significant impact on the properties of electrolytes. Fundamentally, the anionic solvation structure is primarily governed by weak interactions such as hydrogen bonding. As seen in Fig. 3a and Supplementary Fig. 15, the glycerol (C3H8O3) and boric acid (H3BO3) molecules show higher binding energy (−0.30 eV for C3H8O3 and −0.32 eV for H3BO3) and higher bond order of H···F (0.171 for C3H8O3 and 0.178 for H3BO3) when interacting with BF4− anions than the H2O molecules with BF4− anions (0.134; −0.16 eV). Thus, the function groups of −OH in glycerol, −OH in boric acid, −CONH2 in PAM, and especially −OH and −NH2 in CS will act as hydrogen bond donors to replace the water molecules around free BF4−, which can also confine the free water molecules and inhibit the water-induced vicious hydrolysis reaction of BF4−. Thereby, the reconstruction and protection of BF4− structures can be realized (Fig. 3d, e and Supplementary Figs. 16, 17). Due to the reconstruction of both cationic and anionic solvation structures, the activation energy also decreases from 43.53 kJ mol−1 for AE electrolyte to 27.02 kJ mol−1 for ZGBCP electrolyte (Fig. 3f and Supplementary Fig. 18), which confirms the above hypothesis. Besides, the transport properties obtained from MD simulations under different temperatures match up with the experimental results well (Supplementary Fig. 19). To elaborate on the role of glycerol in the solvation structures, the DFT calculation further revealed the asymmetric ESP because of the strong hydrogen bond between the central hydroxyl–H and one of the edge hydroxyl–O within the glycerol molecule as shown in the inset of Supplementary Fig. 20b30,31,32. Therefore, the desolvation zone and solvation zone are able to exit independently and convert rapidly thanks to the intramolecular hydrogen bond with short life, which guarantees the fast cationic solvation and desolvation process compared to other polyols (Supplementary Fig. 20)33,34,35. Besides, the stronger anionic affinity of boric acid, glycerol, and CS is also conducive to the transfer process of cations, which interprets the high transfer number (0.82) and much lower desolvation energy barrier (3.46 eV) of Zn2+ in the ZGBCP electrolyte as shown in above Fig. 3g and Supplementary Fig. 20f36.Thanks to the desolvation acceleration and suppression of free waters from attacking BF4−, the LSV tests showed a HER threshold potential expansion from −0.17 V for the AE to −0.50 V for the ZGBCP electrolyte. In contrast, the HER potentials for the ZCP and ZGP electrolytes are only −0.29 and −0.33 V, respectively according to Fig. 3h. To further verify this phenomenon from a spectral version, a series of spectra tests were conducted. First, the ATR-FT-IR spectra revealed the tuned F···H−O−H interactions and stronger B−F bonds in the ZGBCP electrolyte compared to the other electrolytes (Supplementary Fig. 21). The elevated electron density in F sites of BF4- anions with the addition of boric acid was also observed from the 19F NMR spectra (Supplementary Fig. 22). Besides, a lower HF content was found in the XPS F1s results as shown in the Supplementary Fig. 23b, which are crucial for the interfacial stabilization of the Zn anodes. In conclusion, the CRACSS strategy is expected to improve the long-term cycling ability of Zn(BF4)2-based electrolytes towards AZMBs based on the above theoretical and experimental analysis.Investigations of interface behavior of Zn anode matched with different electrolytesAs analyzed above, the ZGBCP electrolyte with robust adhesion, high conductivity, and low HER risk was constructed by the CRACSS strategy successfully. To additionally verify the effectiveness from the perspectives of interfacial behavior, the HER tests of Zn anode with different electrolytes were characterized by in-situ optical microscopy (Supplementary Fig. 24). It is obvious that even in a quiescent state, vigorous gas evolution occurred at the Zn/AE interface due to the intense hydrolysis of BF4−. In contrast, no gas was observed for the Zn/ZGBCP interface, indicating that ZGBCP is capable of suppressing the HER side reaction. Furthermore, the ZGBCP electrolyte exhibited the fastest 3D diffusion behavior during the Zn plating process (Supplementary Fig. 25a), which benefits from the intimate interfacial adhesion and accelerated desolvation process as proved above. The smallest differential capacitance as illustrated in Supplementary Fig. 25b also confirmed the suppression of concentration polarization, which coincides with the results of the lowest adsorption/desorption, charge transfer, and diffusion impedance of the distribution of relaxation times (DRT) spectra of Zn||Zn symmetric cells using ZGBCP electrolyte in Supplementary Fig. 25c.From Fig. 4a, it can be seen that the symmetric cell based on ZGBCP electrolyte achieved stable cycling for over 3000 h at a current density of 1 mA cm−2. In contrast, the cells using AE, ZGP and ZCP electrolytes occur short-circuiting after only about 100 h. In addition, optical profile images (Supplementary Fig. 26) and SEM images (Supplementary Fig. 27) of Zn anodes revealed the lower surface roughness (Ra = 6.76 μm) and the smoother surface without dendrites or side reaction products for the Zn electrode after cycling with ZGBCP electrolyte, suggesting its excellent compatibility with Zn anodes. On the other hand, for the Zn plating behavior, the XRD patterns of the cycled Zn anodes with different electrolytes were collected and shown in Fig. 4b. The cycled Zn anode with ZGBCP electrolyte exhibited a strong (002) preferential orientation with an I(002)/I(101) ratio as high as 2.20, indicating ZGBCP electrolyte can induce the preferential plating behavior and alleviate the dendritic short-circuiting, which is consistent with the previous reports that also use solvation structure regulation strategies37, 38. Furthermore, Tafel tests, as illustrated in Supplementary Fig. 25d, prove that the ZGBCP electrolyte exhibited exchange current densities nearly comparable to AE electrolyte, demonstrating the ZGBCP electrolyte offers ultra-fast stripping/plating reaction kinetics. As a result, when using the ZGBCP electrolyte, the polarization voltage of the Zn||Zn symmetric cell (Fig. 4c) is lower than that of the cell with other electrolytes. Moreover, even at a high current density of 10 mA cm−2, the polarization voltage is only 215 mV.Fig. 4: Interfacial stripping/plating reaction kinetics and interfacial SEI of Zn anode with different electrolytes.a Cycling stability of the Zn||Zn symmetric cell (1 mAh cm−2, 1 mA cm−2). b XRD spectra of Zn anodes using different electrolytes after 100 cycles. c Rate performance tests of Zn||Zn symmetric cells with different electrolytes. d Binding energy of between F− with H2O, boric acid, and glycerol molecules based on the B3LYP/6-311 ++ g(d,p) level DFT calculations. e, ATR-FT-IR spectra at the Zn anodes surface using ZGBCP, ZCP, and AE electrolytes. f XPS spectra of Zn 2p of Zn anodes at different depths. g The profiles of the atomic percentage of Zn and F atoms versus etching time. h DRT spectra of the Zn||Zn symmetric cells tested at different temperatures from −40 to +50 °C. i Comparison of polarization voltages of Zn||Zn symmetric cells at different current densities of reported Zn(BF4)2-based electrolytes and this work4, 15, 16, 37, 39,40,41,42,43,44.Furthermore, the ZGBCP electrolyte can alleviate the corrosion reaction, which is attributed to the reconstruction of the anionic solvation structure and the capturing of the free F− anions by the glycerol and boric acid (Fig. 4d). Thus, the ATR-FT-IR spectra of the Zn anode interface after cycling with ZGBCP electrolyte shows a weaker Zn−F stretching vibration signal and a stronger B−F stretching vibration signal, indicating less transformation of BF4− into ZnF2 (Fig. 4e). In addition, unlike the uneven corrosion layer on the Zn anodes surface after cycling with the AE electrolyte, the SEI at the Zn/ZGBCP interface is denser and has a more uniform F distribution of ~5 nm (Supplementary Figs. 28 and 29). To further elucidate the mechanism of SEI formation promoted by ZGBCP electrolyte and its structure-performance relationship, XPS tests were conducted at different depths of the Zn electrode etched by Ar+ beams. As seen in Fig. 4f and Supplementary Figs. 30, 31, a thinner and more homogenous SEI is generated on the Zn electrode after cycling using the ZGBCP electrolyte and exhibits lower fluorine and higher zinc content compared to the SEI that lacks Zn2+ for the Zn electrode cycled in the AE electrolyte. As a result, the optimized Zn2+-rich SEI can provide a shorter solid-phase mass transport path and avoid concentration polarization on the basis of protecting Zn electrodes (Fig. 4g).In order to understand the balance between the kinetics and anti-corrosion of Zn stripping/plating process endowed by the ZGBCP electrolyte and clarify the different roles of glycerol, boric acid and chitosan in the electrolyte, Tafel tests of Zn electrode paired with different electrolytes were conducted under different temperatures from −40 to +50 °C (Supplementary Fig. 32). Among all the electrolytes, AE electrolyte showed the most rampant corrosion and HER reactions at +50 °C. Furthermore, the most balanced level of exchange current density along with equilibrium potential at −40 °C was observed using ZGBCP electrolyte thanks to the lowest energy barrier of desolvation, optimized SEI, and robust adhesion. The DRT spectra of the Zn||Zn symmetric cells using AE and ZGBCP electrolyte further corroborate this conclusion, since the diffusion and charge transfer impedance increase more dramatically along with the decrease of temperature for the AE electrolyte (Fig. 4h). It needs to point out that the polarization voltage can be further decreased to 190 mV at 10 mA cm−2 (Supplementary Fig. 33) and is as low as 280 mV at ultralow temperature of −40 °C (Supplementary Fig. 34) when using an electroplated Zn electrode, which is the record-low value among all the reported electrolytes using Zn(BF4)2 salt (Fig. 4i)4, 15, 16, 37, 39,40,41,42,43,44. In summary, the perfect balance of stripping/plating kinetics and interfacial SEI endowed by the ZGBCP electrolyte indicate the five components of glycerol, boric acid, CS, PAM, and Zn(BF4)2 in the electrolyte play synergistic roles in regulating solvation structures and decreasing polarization. This paves the way for ultra-stable AZMBs even under a wide working temperature range.The electrochemical performance of the full cells with different electrolytesAs mentioned above, the CRACSS strategy effectively regulates both the cationic and anionic solvation structures. To verify the influences of the CRACSS strategy on electrochemical performance, polyaniline (PANI), which can store both anions (BF4−) and cations (Zn2+), was selected as the cathode to investigate the compatibility and effect of ZGBCP electrolyte. Impressively, as seen from Fig. 5a, the Zn|ZGBCP|PANI full cell exhibited better rate performance, and a reversible specific capacity exceeding 140 mAh g−1 was achieved at a current density of 0.2 A g−1 (Fig. 5b). Even at a high current density of 20 A g−1 (corresponding to 35 mA cm−2), the specific capacity remained as high as 120 mAh g−1. The full cell with AE electrolyte showed fast capacity decay upon increasing rates, while the coulombic efficiency (CE) and energy efficiency (EE) of the full cells were well maintained when using the ZGBCP as the electrolyte (Supplementary Fig. 35a, b). In particular, a comprehensive comparison between the reported Zn||PANI batteries with this work reveals that the Zn|ZGBCP|PANI full cell possesses higher energy and power density as illustrated in Supplementary Fig. 35c. In addition, the full cell with ZGBCP electrolyte demonstrated ultralong cycling stability of over 10,000 cycles at a high rate of 15 A g−1 (Fig. 5c) and almost same polarization and diffusion coefficient as the liquid cell (Supplementary Fig. 35d). Moreover, for conversion-type electrode reactions based on halides shown in Supplementary Fig. 36, the ZGBCP electrolyte also renders the cathode excellent reversibility. Even at a high current density of 15 A g−1, the Zn|ZGBCP|I2 full cell provided a specific capacity of 124 mAh g−1 after 12,000 cycles, demonstrating the universality of the ZGBCP electrolyte.Fig. 5: Electrochemical performance and reaction mechanism analysis of Zn||PANI full cells with different electrolytes.a Rate performance of full cells. b Charge and discharge profiles of the full cell using ZGBCP electrolyte at different current densities. c Cyclic performance of the full cell using ZGBCP electrolyte at 15 A g−1. d CV curves of full batteries using AE and ZGBCP electrolytes. e log (ip) versus log (v) profile. f Energy level of the representative cationic (left) and anionic (right) solvation structures from AE and ZGBCP electrolytes based on the B97-3c level DFT calculations. g In-situ DRT spectra of the full cells using the ZGBCP and AE electrolytes at different voltages. h In-situ DRT spectra of full cells using different electrolytes.In order to clarify the underlying mechanism of improved kinetics by the ZGBCP electrolyte, a series of electrochemical and spectroscopic analyses was conducted. The cyclic voltammetry (CV) curves of Zn|ZGBCP|PANI full cells using different electrolytes were compared in Fig. 5d and Supplementary Fig. 37. The full cell with ZGBCP as the electrolyte shows the most well-defined, lowest polarization, and highest anodic/cathodic peak current. Moreover, the main cathodic peak potential barely shifted as the scan rate gradually increased from 1 to 10 mV s−1 as illustrated in Fig. 5e and Supplementary Fig. 38, indicating that ZGBCP significantly enhances the reaction kinetics of the PANI cathode. Based on the Eq. (3):$$i=k{v}^{{\rm {b}}}$$
(3)
the peak current–peak potential relationship was linearly fitted, yielding a b value close to 1, indicating the surface capacitive control of the anionic/cationic coordination reaction, which is consist with the dominant pseudocapacitive contribution.Thorough DFT calculations were further conducted to analyze the solvation structures of cations and free anions. As seen from Fig. 5f and Supplementary Fig. 39, there are dramatic reductions in the energy gap exceeding 1–2 eV for all the cationic solvation structures in the ZGBCP electrolyte. The elevated active electron states can further facilitate (de)solvation and accelerate charge transfer during the charge and discharge process, enhancing the electrochemical reactivity45. Besides, the elevated HOMO levels of the anionic solvation structures dominated by other ligands instead of H2O are beneficial for the charging process of PANI, which can also alleviate the irreversible water and proton consumption during the cycling as seen in Supplementary Fig. 40. To further analyze the reaction kinetics of the cathode, in-situ EIS tests were conducted using different electrolytes, and the corresponding DRT spectra were obtained as shown in Fig. 5g, h. Remarkably, the ZGBCP electrolyte showed almost no charge transfer impedance in the cathode side from the range of 0.1 ~10 s and a much lower diffusion impedance compared to the AE electrolyte according to Fig. 5g, which is consistent with the lower polarization observed in the CV curves between Peaks 1 and 2. On the other hand, due to the superior interface adhesion macroscopically, optimized SEI microscopically, and lower desolvation energy barrier in the molecular scale tuned by the CRACSS strategy, the full cell using ZGBCP electrolyte exhibits almost no charge transfer impedance on the Zn anode side during the whole charge and discharge process in comparison with AE. At room and elevated temperature, it can be seen from Supplementary Fig. 41 that the chain structures of PANI cathode decompose faster with ZCP electrolyte, which is proved by the N 1s XPS, UV–Vis, and RAMAN spectrums. In contrast, the structures of the PANI cathode are well maintained when using ZGBCP electrolyte, indicating its capability of enhancing the thermal stability of the PANI cathode.Since the ZGBCP is stable in a wide temperature, the Zn|ZGBCP|PANI full cell was then evaluated at various temperatures. As seen from Fig. 6a, the cell can stably operate from −50 to +100 °C and deliver decent specific capacities of 103.1 and 100.7 mAh g−1 at −50 and +100 °C, respectively. Furthermore, whether at low temperatures (−40 and −50 °C) or elevated temperatures (+50 °C), the ZGBCP-based full cells all exhibit excellent rate capability (Fig. 6b and Supplementary Fig. 42), and the specific capacity can well-recover under the transition of low temperatures and elevated temperatures. Such a wide working temperature is superior to the so-far reported hydrogel-based AZMBs, as shown in Fig. 6e27, 42, 46,47,48,49,50,51,52,53,54,55,56,57,58,59, indicating the most advanced cell performance rendered by the ZGBCP electrolyte. As mentioned, the PANI suffers from thermal decomposition and even HER at elevated temperatures, which can be seen from the CV and GCD curves using AE in Supplementary Fig. 43. However, when matched with ZGBCP electrolyte, it can stably cycle for 300 cycles even at +80 °C, suggesting ZGBCP is indeed capable of inhibiting the high-temperature decomposition as shown in Supplementary Fig. 43c.Fig. 6: Electrochemical performance of Zn|ZGBCP|PANI full cells at extreme temperatures.a Charge and discharge profiles under different temperatures from −50 to 100 °C at 1 A g−1. b Cycling performance at −40/50 °C. c Long-term cycling performance at −40 °C at 10 A g−1. d Long-term cycling performance at 50 °C at 15 A g−1. e Comparison of the temperature windows of the reported AZMBs with different electrolytes27, 42, 46,47,48,49,50,51,52,53,54,55,56,57,58,59. f Demonstration of electronic devices powered by three pouch-cells in series at −40 and 70 °C. g Summary of the regulation mechanism based on the CRACSS strategy in the full cells.As to long cycling stability, the full cell shows more impressive performance. At −40 and +50 °C, cycle life up to 30,000 cycles and 5000 cycles with a capacity retention rate of 85.4% and 91.3%, respectively, can be achieved (Fig. 6c, d). Moreover, the specific capacity is even higher than 200 mAh g−1 at +50 °C due to the thermal activation and inhibited HER by the CRACSS strategy. Intriguingly, a wearable electronic device can be powered easily by three Zn|ZGBCP|PANI pouch-cells in series even at −40 and 70 °C, as displayed in Fig. 6f and Supplementary Fig. 44, which proves the effectiveness and practicality of the CRACSS strategy. Different from the various reported works aiming at AZMBs with wide temperature range through replacing anti-freezing solvent46, 47, 50, 51, 53,54,55, tuning concentration of chaotropic salts42, 49, 58, improving electrodes adhesion27, 52, 57, and modifying ions transport behavior56, 59, the CRACSS strategy is a state-of-art approach with combining properties (Fig. 6e). In conclusion, based on the dual cross-linking framework with robust adhesion and faster motion of chain segments as designed, the reconstruction of the cationic solvation structure enables the ZGBCP electrolyte to suppress the vicious HER and accelerate the stripping/plating kinetics of Zn anodes. Furthermore, the anionic solvation structures are reconstructed to prevent the corrosion induced by the BF4- decomposition and accelerate the charge transfer process towards cathodes, enabling the ZGBCP electrolytes for ultra-stable and ultrawide-temperature-range AZMBs (Fig. 6g).
Reconstruction of zinc-metal battery solvation structures operating from −50 ~ +100 °C