5,10,15,20 Tetrakis [4-(hydroxyl) phenyl] porphyrin [TPHPP] was prepared by condensing pyrrole and 4-hydroxybenzaldehyde in propionic acid44. Metalation of porphyrin with CoCl2·6H2O in DMF form [Co(II) TPHPP]45. Simultaneously the amino group of biopolymer chitosan was protected by using phthalic anhydride forming N-Phthaloyl chitosan46, which chloroacetylated using chloroacetyl chloride in the presence of triethyl amine forming Chloroacetylated N-phthaloyl chitosan46. [Co(II) TPHPP] covalently bonded to (chlorocetylated N-phthaloyl chitosan) by refluxing in the presence of potassium carbonate48. Then, the protected (phthaloyl group) was removed using Hydrazine monohydrate49. Finally, Chitosan/[Co(II) TPHPP] mixed, vigorously stirring with Graphene Oxide suspended solution to form [Co(II) TPHPP]-Cs/GO nanocomposite51 as shown in (Supplementary Figs. S1–S7) Fig. 2.Figure 2The schematic illustration of the prepared [Co(II) TPHPP]-Cs/GO nanocomposite.Structural characterizations and morphologies analysisFT-IR analysisThe FTIR spectrum of THPP is consistent with its chemical structure as shown in (Fig. 3a). The stretching vibrations of O−H and N−H groups showed a broad band at ν 3423 cm−1. Additionally, the peaks at ν 1228 and 1169 cm−1 were attributed to C−N stretching vibrations of amine groups, while peaks at ν 1599 and 1469 cm−1 were assigned to N–H bending and C=N vibrations, respectively. Finally, the peak at ν 808 cm−1 was referred to as the macrocycle ring’s N–H out-of-plane bending vibration. In the [Co(II) THPP] spectrum (Fig. 3b), the peak at ν 3423 cm−1 became broad and slightly shifted to 3420 cm−1. The new peak at ν 1001 cm−1 has appeared, which is characteristic absorption of the Co–N(equatorial) bond formed in [Co(II) THPP]24,53.Figure 3FT IR spectra of (a) [TPHPP], (b) [Co(II) TPHPP], (c) Chitosan, (d) N-Phthaloyl Chitosan, (e) acetylated N-Phthaloyl Chitosan, (f) [Co(II) TPHPP]-N-Phthaloyl Chitosan, (g) [Co(II) TPHPP]-Chitosan, (h) Graphene oxide, (i) [Co(II) TPHPP]-Cs/GO nanocomposite.The spectrum of Cs (Fig. 3c) shows a broad band at ν 3424 cm−1, which is the region where the stretching vibration of O−H and N−H groups are situated due to intermolecular H-bond. The absorption bands at ν 1634 cm−1 and 1389 cm−1 correspond to the C=O stretching vibration (amide band) and C−N stretching vibration in amide. And band at ν 1069 cm−1 corresponds to C−O stretching vibration. Unlike chitosan, the FT IR spectrum of N-phthaloyl chitosan (Fig. 3d) exhibits characteristic peaks at ν 1715, 1759 corresponding to C=O of the phthalimide group. And another peak at ν 1555 and 724cm−1 for C=C stretching vibration and C−H bending vibration of an aromatic ring54.For the chloroacetylated of N-phthaloyl chitosan (Fig. 3e), a new signal around ν 2958 cm−1 (methylene of the chloroacetyl group) was found to correlate with the decrease of the signal around ν 3424 cm−1 (hydroxyl groups). Also, a new peak at ν 717 cm−1 confirmed the presence of C–Cl in the chloroacetyl group55,56,57.For [Co(II) TPHPP] supported on N-Phthaloyl chitosan spectrum (Fig. 3f), the broad peak around at ν 3486 cm−1 was slightly shifted to ν 3432 cm−1, and the intensity was diminished which related to vibration of O−H and N−H groups. Also, the band at ν 1759 and 1715 cm−1 was shifted at ν 1720 and 1661 cm−1, and the significant peak at ν 717 cm−1 which is related to C–Cl in the chloroacetyl group disappeared due to attaching [Co(II) THPP] 1 to N-phthaloyl chitosan. This proves that the [Co(II) THPP] 1 molecules were covalently bonded to N-phthaloyl chitosan. As seen, signature bands for [Co(II) THPP] did not appear anywhere in the spectrum of [Co(II) THPP]–N-phthaloyl chitosan due to the overlap of the spectra of N-phthaloyl chitosan and [Co(II) THPP] in the entire infrared region58.FT-IR spectrum for the protected group (phthaloyl group) removed (Fig. 3g), chitosan/Co-porphyrin show disappearing characteristic peaks at ν 1720,1661,717 cm−1 correspond to C=O of phthalimide group and C−H bending vibration of aromatic ring. Another peak appeared at ν 1656 cm−1 this evidence removed the protected group (phthalic anhydride)59.The spectrum of GO shown in (Fig. 3h), exhibited a broad band at 3442 cm−1 for O–H groups, and two characteristic bands for C=O and C=C at 1720, and 1627 cm−1, respectively. Furthermore, the other peaks corresponding to C–OH and C–O stretching vibration appeared at 1387 and 1074 cm−1, respectively. These characteristic peaks indicated that the GO nanosheets were successfully synthesized60.The final FT-IR spectrum of [Co(II) TPHPP]-Cs/GO nanocomposite (Fig. 3i), starching vibration of C=O in amide downshift from ν 1651 to 1632 cm−1, and NH2 deformation vibration downshift from ν 1438 to 1431 cm−1. indicate an amide bond between NH2, and COOH, This evidence for the formation of an amide bond (–NHCO–)61.XRD structural characterizationThe X-ray powder diffraction pattern was illustrated in Fig. 4 where (Fig. 4a) the original chitosan shows a weak peak at 2θ = 9.60° and a more intense peak at 2θ = 20.22° that is caused by diffraction from the (020) and (110) planes of the crystalline lattice with interplane distances of 0.92 nm and 0.438 nm, respectively. It is worth noting that the corresponding degree of acetylation was 81% and its crystalline index was 5562,63,64,65.Figure 4X-ray pattern of (a) Chitosan, (b) N-Phthaloyl Chitosan, (c) N-Phthaloyl Chitosan-[Co(II) TPHPP], (d) Chitosan-[Co(II) TPHPP], (e) Graphene Oxide, (f) [Co(II) TPHPP]-Cs/GO nanocomposite.N-phthaloyl chitosan (Fig. 4b) showed the disappearance of the peak at 2θ = 9.6° with the appearance of another peak at 6.42°, and the peak at 2θ = 20.22° was shifted to 2θ = 18.62°. This explains why the amount of hydrogen bonds decreased by blocking amino groups, leading to a typical diffraction pattern with lower crystallinity. It was reported that N-phthaloyl chitosan prepared in DMF/water showed a certain crystallinity, despite the introduction of the phthaloyl group; this also supports the uniform structure of the product. It is noteworthy that N-phthaloyl-chitosan exhibited certain crystallinity even though such a bulky substituent had been introduced64.N-Phthaloyl chitosan-[Co(II) TPHPP] shows a more broadening peak at around 2θ = 22.8° (Fig. 4c). The addition of [Co(II) TPHPP] to N-Phthaloyl Chitosan reacts with the hydroxyl group, further decreasing crystallinity where no more hydrogen bonding exists66.Figure 4d shows that the deprotection of the amino group of chitosan (phthaloyl group) shows a characteristic peak at 2θ = 20.81°, which indicates a higher crystallinity of this compound.Figure 4e show a sharp peak at 2θ = 10.32°, which confirms that graphite powder was oxidized well, utilizing concentrated acids and KMnO4 to obtain GO. After modifying GO with modified [Co(II) TPHPP]-Cs, the significant peak of GO at 2θ = 10.32° shifted to a smaller angle and appeared at 2θ = 9.60° as shown in (Fig. 4f). This shift is due to the intercalation of GO by modified metalloporphyrin-chitosan chains. The two peaks of Cs are not observed in the XRD patterns of GO-Cs nanocomposite, indicating that [Co(II) TPHPP]-Cs chains are well intercalated amongst the GO sheets. This confirms the good attachment of [Co(II) TPHPP]-Cs to GO layers67,68.SEM and TEM analysisOne of the most important factors affecting the heterogeneous catalysis behavior is the morphological characteristics of their surface. Therefore, the interfacial interactions between [Co(II) TPHPP]-Chitosan and Graphene Oxide can change the surface morphology of the obtained nanocomposite.SEM and EDX techniqueSEM micrograph of the [Co(II) TPHPP] supported on chitosan before and after GO incorporation, where the uniform distribution of [Co(II) TPHPP]-chitosan network is displayed in (Fig. 5a). The typical morphology of GO is shown in (Fig. 5b), which has a smooth, flat, soft surface and many layers stacked on top of one another in a range of sizes and forms. Furthermore, as seen in (Fig. 5c,d), the irregularly shaped GO layers and their surface developed wrinkles as a result of being occupied by [Co(II) TPHPP]-Cs beads, where the [Co(II) TPHPP]-Cs beads bind the bunches of flake GO sheets, these bound transpire on the surface and from edges confirm the tightly bound with each other and illustrate the successful interaction between [Co(II) TPHPP]-Cs and the GO. Additionally, similar results were supported using the EDX analysis, which shows the presence of elements such as C, O, and N, Co, which indicate the combination between them forming [Co(II) TPHPP]-Cs/G’O nanocomposite in (Fig. 5e).Figure 5Scanning electron microscope (SEM) analysis of [Co(II) TPHPP]-Cs (a), Graphene Oxide (b), [Co(II) TPHPP]-Cs/GO nanocomposite (c,d), and (e) indicating the elements by EDX analysis.TEM analysisThe TEM imaged in (Fig. 6a,b), shows the nanoparticles morphologies of [Co(II) TPHPP]-modified Chitosan are mostly spherical. Some of these beads spread and others aggregated within Graphene Oxide layers. The TEM image shows that the changes to the inner layers of GO are dramatic and clearly visible as some layers intercalated and others exfoliated. Where the bulk of GO sheets contain beads with wrinkles due to the dispersion of [Co(II) TPHPP]-chitosan networks on the GO sheets. Figure 6c shows the histogram of the particle size distribution curve of [Co(II) TPHPP]-Cs/GO nanocomposite where the irregular spherical shape of these beads and its average particle size (< 30 nm).Figure 6Transmission electron microscope (TEM) analysis of [Co(II) TPHPP]-Cs/GO nanocomposite (a,b), and (c) Histogram of particle size distribution curve of [Co(II) TPHPP]-Cs/GO nanocomposite from (TEM).Catalytic oxidation of AO7The catalytic oxidation of (AO7) has been investigated using hydrogen peroxide as an oxidant and [Co(II) TPHPP]-Cs/GO nanocomposite as a catalyst in aqueous solution. The oxidation reaction was followed by recording the UV–Vis spectra of the reaction mixture with time at λmax = 485 nm. (Fig. 7a) represents the collapse of the main absorbance band of AO7 at λmax = 485 nm almost vanished, and the degradation percent of AO7 reached 94% within 60 min, this is due to the lost conjugation in the dye leading to colorless oxidation products. This reverberates an essential role of using H2O2 and [Co(II) TPHPP]-Cs/GO nanocomposite in the degradation of AO7. Figure 7b also shows the kinetic curve for the destruction of AO7, the plot of (lnA0/At) against time presents a straight line, this indicates that the degradation of AO7 is considered a first-order rate kinetic69,70 and it could be simply described as ln A0/At = kobs t.Figure 7(a) Electronic absorption spectra during decolorization of AO7, (b) First-order plot for the degradation of AO7 with (kobs = 0.236 min−1). For reaction conditions: AO7 (1.42 × 10−4 M) with H2O2 (8 × 10−2 M) in the presence of [Co(II) TPHPP]-Cs/GO nanocomposite (15 × 10−3 g/mL) and pH = 9 at 40 °C.Before studying the behavior of this supported catalyst, it is important to evaluate the AO7 decolorization process, i.e., whether AO7 removal occurs through adsorption, through a catalytic reaction, or both processes. For that reason, several runs were then performed. The first one was a blank, carried out to evaluate the ability of H2O2 to eliminate AO7 in aqueous solutions without the addition of the heterogeneous catalyst which shows that AO7 degradation due to hydrogen peroxide is almost negligible (Supplementary Fig. S8) which might be attributed to its low oxidation potential as compared to hydroxyl radicals.To determine the influence of the adsorption processes experiment without, H2O2 and in the presence of [Co(II) TPHPP]-Cs/GO nanocomposite was carried out as shown in (Supplementary Fig. S9) and also carried out at different pH used (7,9 and 11) (Supplementary Fig. S10), which indicated no significant decolorization of dye, this evidence for the degradation pathway occurred through a catalytic reaction.Influence of the experimental conditions on oxidation of AO7The factors that may influence the oxidation of AO7, such as the Influence of reaction pH, AO7, concentration of catalyst, hydrogen peroxide, and temperature have been investigated.Influence of initial PHThe influence of pH on the oxidation reaction was investigated at a constant concentration of the dye (1.42 × 10–4 M), H2O2 (8 × 10−2 M) as well as a fixed amount of [Co(II) TPHPP]-Cs/GO nanocomposite (15 × 10–3 g/mL) at 40 °C. The pH varied in the range of 7–11. Data illustrated in (Fig. 8) show that the decolorization of AO7 increased with an increase of pH and reached optimum at pH = 9.071,72. The factors likely responsible for the decrease in the observed rate of constant kobs at higher pH are the formation of hydroperoxide anion HO−2 in an alkaline medium, which reacts with the non-dissociated molecule of H2O2 according to reaction Eq. (3).$$ {{\text{H}}_2}{{\text{O}}_2} + {\text{HO}}_2^- \to {{\text{H}}_2}{\text{O}} + {{\text{O}}_2} + {\text{H}}{{\text{O}}^- } $$
(3)
Figure 8Effect of pH on the decolorization of AO7. The pH was adjusted to 8 and 9 using borax and HCl buffer mixture and the pH was adjusted to 10.0 using NaHCO3 and NaOH mixture. Phosphates were used to adjust the pH to 7 and 11.Influence of AO7 concentrationThe variation of the decolorization efficiency of the AO7 with H2O2 and [Co(II) TPHPP]-Cs / GO nanocomposite with varying the concentration of the dye from 6.65 × 10−5 M to 2.85 × 10−4 M. (Fig. 9) shows that the decolorization efficiency reduces with a further increase in dye concentration. This phenomenon may be attributed to the high concentration of AO7 molecules that may aggregate on the catalyst surface and inhibit contact between H2O2 and the catalyst, which reduces the number of hydroxyl radicals involved in the decolorizing process72. The molar ratio oxidant/dye is low (because the amount of hydrogen peroxide molecules initially present in the reaction is the same).Figure 9Effect of AO7 concentration on decolorization process.Influence of catalyst concentrationData illustrated in (Fig. 10) show that the rate of oxidation of AO7 increases with an increase of the catalyst concentration from 4 × 10−3 g/mL to 15 × 10−3 g/mL with all other reaction parameters fixed, at 40 °C. This may be attributed to the increase in the number of available active sites on the catalyst surface for H2O2 activation and the increased rate of formation of hydroxyl radicals73. After 15 × 10−3 g/mL concentration, adding more catalyst may not have a significant effect on the rate of reaction. This point is called steady-state concentration where no further increase in the rate of reaction, due to the limited number of attacking active species involved in the degradation process, kobs remained almost constant. Thus, the optimum catalyst dosage74.Figure 10Effect of catalyst concentration on decolorization process.Influence of initial H2O2 concentrationThe effect of the concentration of H2O2 on the oxidation of AO7 was analyzed by varying its initial concentration between 1.6 × 10−2 M and 12.94 × 10−2 M at 40 °C (Fig. 11). Increasing H2O2 concentration from 1.6 × 10−2 M to 8.08 × 10−2 M increases the rate of decolorization of the dye AO7 because more •OH radicals are formed. A further increase in the concentration of H2O2 partly inhibited the oxidation rate due to the well-known hydroxyl radicals scavenging effect. The undesirable reactions (4) and (5) compete with the destruction of the dye chromophore72. These reactions reduced the probability of attacking the AO7 molecules by hydroxyl radicals, which decreased the decolorization rate of the dye at a high concentration of H2O2.$$ {{\text{H}}_2}{{\text{O}}_2} + {}^ \cdot {\text{OH}} \to {\text{HO}}_2^ \cdot + {{\text{H}}_2}{\text{O}} $$
(4)
$$ {\text{HO}}_2^\cdot + {}^\cdot {\text{OH}} \to {{\text{H}}_2}{\text{O}} + {{\text{O}}_2} $$
(5)
Figure 11. Effect of concentration of H2O2 on the decolorization of AO7.Influence of reaction temperatureThe effect of temperature on the decolorization of AO7 with [Co(II)-TPHPP]-Cs/GO nanocomposite /H2O2 has been studied in the range of 25–55 °C. (Fig. 12) shows that the decolorization rate increased with an increase in reaction temperature. Increasing temperature led to a shorter time for decolorization of AO7.Figure 12Effect of temperature on the decolorization of AO7.Thermodynamic parameters for degradation AO7 such as Gibbs free energy (ΔG°), enthalpy (ΔH°), and entropy (ΔS°) describe the nature and type, and disorder of the system at the liquid–solid interface75.Data illustrated in Table 1 where: a positive ∆G° value validates a non-spontaneous process under standard conditions, which means that the reaction still prefers reactants over products under the given conditions. Overall, a positive ΔG with a catalyst doesn’t necessarily mean an ineffective reaction. It just means the reaction leans toward the reactants, and the catalyst helps achieve equilibrium faster76,77. A positive ∆H° value is indicative of an endothermic, irreversible process, and the negative value of ΔS° revealed that the degree of the disorder decreased at the solid–liquid interface during the reaction and the positive Ea is an indication the system requires energy (increased temperature) to drive the process, therefore is termed endothermic78.Table 1 Rate constant and activation parameters of catalytic degradation of AO7 by [Co(II) TPHPP] -Cs / GO nanocomposite with H2O2.Mineralization and proposed degradation pathway of AO7Total organic carbon analysis (TOC) is an important method for evaluating the mineralization of the oxidative degradation reactions of dyes. Oxidation of AO7 under standard reaction conditions at 40 °C showed after 60 min TOC removal of 50% indicating incomplete mineralization of the dye to CO2 and H2O. However, raising the reaction temperature to 55 °C mineralization of the dye increased and the mineralization of AO7 also enhanced with a higher concentration of catalyst up to 15 × 10–3 g/mL79,80,81,82.To further evaluate the efficiency of the catalytic [Co(II) TPHPP]-Cs/GO nanocomposite with an H2O2 system, Gas chromatography-mass spectrometry (GC–MS) analysis, was employed to study the degradation behavior of AO7 and identify the residual organic intermediate products at different retention times as shown in Table 2, compounds such as β-naphthol, naphthalene-1,4-dione, 4-azo benzenesulfonate, (E)-3-(2-formyl-4-hydroxy-3-nitrophenyl)-3-hydroxyacrylic acid, 2-hydroxy-8-nitronaphthalene-1,4-dione, 5-nitronaphthalene-1,4-dione were separated at t = 30 min. In addition to phthalic acid, isobenzofuran-1,3-dione, and 2-formyl benzoic acid were separated at t = 60 min. lastly salicylic acid, pyrocatechol, cyclopenta-2,4-dien-1-ol, benzenesulfonate, phenol was separated at t = 120 min. These compounds have been found as a common product that came from the degradation of AO7 in the reported literature83,84,85,86.Table 2 Identified reaction intermediates degradation of AO7 by GC–MS.Comparison with other systemsTable 3 compared the results obtained in terms of catalytic degradation efficiency, stability, reaction time, temperature, pH, and dye mineralization of AO7 in the presence of the [Co(II) TPHPP]-Cs/GO nanocomposite presented in this work, to other previously published results. It can be seen from Table 3. A heterogeneous catalyst used [Co(II) TPHPP]-Cs/GO nanocomposite gave higher degradation yield and mineralization of AO7 with a shorter reaction time required and also showed high catalytic stability and no significant changes up to the six-run compared to the other heterogeneous catalysts used in the comparison.Table 3 Comparison of [Co(II) TPHPP]-Cs/GO nanocomposite with other heterogeneous systems.Identification of reactive oxygen species (ROS)Hydroxyl radical analysis using isopropyl alcoholHydroxyl radicals were able to be the reactive species in the oxidation of the dye AO7 by our catalytic system [Co(II) TPHPP]-Cs/GO nanocomposite/H2O2, hence, the inhibiting effect of isopropyl alcohol as hydroxyl radicals scavenging agent has been investigated on the oxidation reaction of AO7 by H2O2/catalyst. As shown in (Fig. 13), the rate of degradation of AO7 decreased with the addition of isopropyl alcohol to the reaction mixture and was inhibited by increasing the concentration of isopropyl alcohol in the reaction solution. This indicates that decolorization of AO7 by [Co(II) TPHPP]-Cs/GO nanocomposite/H2O2 involved the formation and participation of •OH radicals as the active species.Figure 13Effect of increased isopropyl alcohol on the decolorization of AO7.Hydroxyl radical determinationTo identify the reactive oxygen species formed in the [Co(II) TPHPP]-Cs/GO nanocomposite/H2O2 system, disodium salt of terephthalic acid (NaTA) photo-luminescence probing technology measurements were carried out. NaTA could react with ·OH to give 2-hydroxy terephthalic acid (HTA), which exhibits a bright stable fluorescence91. This reaction is unaffected by the presence of other reactive species such as H2O2, HO2·, and O2·, so it could be used as a sensitive probe in detecting ·OH radicals92. (Fig. 14) shows the fluorescence spectra of the solution containing the [Co(II) TPHPP]-Cs/GO nanocomposite/H2O2-system and NaTA.Figure 14Fluorescent intensity of hydroxy terephthalic acid formed with [Co(II) TPHPP]-Cs/GO nanocomposite/H2O2, in the presence and absence of AO7.It’s observable that the fluorescence intensity increases sharply to 220 within 75 min, implying that •OH radicals were indeed generated in the system. Moreover, when AO7 and NaTA were simultaneously added into the solution, the generated fluorescence significantly decreased, with the intensity only increasing to 80 simultaneously.Suggested mechanismThe suggested mechanism for the oxidation reaction involves an activation of the H2O2 molecule, leading to the formation of hydroxyl radicals(•OH). as shown in the following equations.$$ {\text{S}} – [{\text{Co}}({\text{II}}){\text{TPHPP}}] + {{\text{H}}_2}{{\text{O}}_2} \to {}^\cdot {\text{OH}} + {}^- {\text{OH}} + {\text{S}} – [{\text{Co}}({\text{III}}){\text{TPHPP}}] $$
(6)
$$ {\text{S}} – [{\text{Co}}({\text{III}}){\text{TPHPP}}] + {}^- {\text{OH}} \to {\text{S}} – [{\text{Co}}({\text{II}}){\text{TPHPP}}({\text{OH}})] \to {\text{S}} – [{\text{Co}}({\text{II}}){\text{TPHPP}}] + {}^\cdot {\text{OH}}$$
(7)
$$ {\text{AO}}7 + {}^\cdot {\text{OH}} \to {\text{Residual}}\,{\text{organic}}\,{\text{intermediate}} + {{\text{H}}_2}{{\text{O}}_2} + {\text{C}}{{\text{O}}_2} $$
(8)
where S is the supported nanocomposite, [TPHPP] is the ligand, and Co is the metal ions. Cobalt can be used as a catalyst, preferably in a heterogeneous system. Cobalt is known to undergo Fenton-type reaction and has been used as an activator in the decomposition of H2O2 and the degradation of various dyes72. The suggested mechanism claims that the catalyst activates the H2O2 molecules, leading to the formation of hydroxyl radicals, ·OH93.The latter attacks the dye forming an active intermediate, which decomposes in the rate-determining step giving the final oxidation product.Recovery and recycling of catalystThere is a wide diversity of benefits resulting from using heterogeneous catalysts in the catalytic oxidation process as reducing reaction costs, diminishing waste generation, and bringing about more environmentally and economically saving methods for separation and recycling24,94. [Co(II) TPHPP]-Cs/GO nanocomposite was readily recovered from the solution by simple filtration and recycled for successive reactions after being rained several times with distilled water. Degradation percentages of AO7 were illustrated (Fig. 15).Figure 15Effect of [Co(II) TPHPP]-Cs/GO nanocomposite recycling on the degradation of AO7 dye. Catalyst 15 × 10−3 g/mL; [AO7]: 1.42 × 10−4 M, [H2O2]: 8 × 10−2 M, pH: 9 at 40 °C.The proportion of AO7 degradation after six consecutive cycles was shown in Fig. 15. No significant changes were detected for the first five successive cycles of [Co(II) TPHPP]-Cs/GO nanocomposite, then the foregoing catalyst losses (15%) of its activity in the sixth cycle. The results clearly showed that the mentioned supported catalyst was active in oxidative degradation and could be stable and reused without a significant decrease in activity and selectivity as shown also in FT-IR (Supplementary Fig. S11).
Synthesis and characterization of Co(II) porphyrin complex supported on chitosan/graphene oxide nanocomposite for efficient green oxidation and removal of Acid Orange 7 dye